Intermetallic Growth of Cu6Sn5 as a function of Cu crystallographic orientation

Download (7.87 MB)
thesis
posted on 2021-07-29, 18:02 authored by Ziyun HuangZiyun Huang

The morphologies and growth behavior of Cu6Sn5 intermetallic compound (IMC) formed between Sn-based solder and large-grain polycrystalline Cu substrate were systematically investigated. Hexagonal Cu6Sn5 grains were observed to form at certain reflow condition, which matches well with the literature results for IMC growing on single crystal substrate. The kinetics of IMC growth was also investigated and different mechanisms were proposed for different evolution stages. It was observed that facet formation should be a growth shape rather than an equilibrium shape, and the orientation relationship between Cu and Cu6Sn5 was studied using scanning electron microscope (SEM) and Electron backscatter diffraction (EBSD), and were visualized on inverse pole figure.

History

Degree Type

  • Master of Science in Materials Science Engineering

Department

  • Materials Engineering

Campus location

  • West Lafayette

Advisor/Supervisor/Committee Chair

John Blendell

Advisor/Supervisor/Committee co-chair

Carol Handwerker

Additional Committee Member 2

Eric Kvam

Usage metrics

    Licence

    Exports

    RefWorks
    BibTeX
    Ref. manager
    Endnote
    DataCite
    NLM
    DC